Waya Karma fun Awọn alatako konge (0.02mm, 0.03mm, 0.04mm)
Karma Waya fun konge Resistors(0.02mm, 0.03mm, 0.04mm)
1. Karma alloy
Karma alloy jẹ ti bàbà, nickel, Aluminiomu ati Iron gẹgẹbi awọn paati akọkọ.Awọn resistivity jẹ 2 ~ 3 igba ti o ga ju MENONG.O ni iye iwọn otutu kekere ti resistance (TCR), EMF igbona kekere dipo bàbà, iduroṣinṣin to dara fun akoko pipẹ ati anti-oxidation lagbara.Iwọn iwọn otutu ti n ṣiṣẹ jẹ fife ju MENONG (-60 ~ 300ºC).O ti wa ni o dara fun ṣiṣe itanran konge resistance eroja ati igara.
2. Karma iwọn
Waya: 0.01mm-10mm
Ribbon: 0.05 * 0.2mm-2.0 * 6.0mm
Rinhoho: 0.5 * 5.0mm-5.0 * 250mm
3.Karma Ohun-ini
| oruko | koodu | Akopọ akọkọ (%) | Standard | |||
| Cr | Al | Fe | Ni | |||
| Karma | 6J22 | 19-21 | 2.5 ~ 3.2 | 2.0 ~ 3.0 | bal. | JB/T 5328 |
| Oruko | Koodu | (20ºC) Resistivity (μΩ.m) | (20ºC) Iwọn otutu.Coeff.Of Resistance (αX10-6/ºC) | (0 ~ 100ºC) ThermalEMF vs.Ejò (μv/ºC) | Max.ṣiṣẹ Iwọn otutu (ºC) | (%) Ilọsiwaju | (N/mm2) Fifẹ Agbara | Standard |
| Karma | 6J22 | 1.33 ± 0.07 | ≤±20 | ≤2.5 | ≤300 | >7 | ≥780 | JB/T 5328 |
4. Awọn ẹya ara ẹrọ ti o yatọ ti Karma resistance wire
1) Bibẹrẹ pẹlu Nickel Chromium itanna ooru waya Kilasi 1, a rọpo diẹ ninu awọn Ni pẹlu
Al ati awọn eroja miiran, ati nitorinaa ṣaṣeyọri ohun elo resistance konge pẹlu ilọsiwaju
olùsọdipúpọ iwọn otutu resistance ati agbara elekitiroti ooru lodi si bàbà.
Pẹlu afikun ti Al, a ti ṣaṣeyọri ni ṣiṣe resistivity iwọn didun 1.2 igba tobi
ju Nickel Chromium itanna ooru waya Kilasi 1 ati agbara fifẹ 1.3 igba tobi.
2) Olusọdipúpọ otutu keji β ti okun waya Karmalloy KMW kere pupọ, - 0.03 × 10-6/ K2,
ati awọn resistance otutu ti tẹ wa ni jade lati wa ni fere kan ni ila gbooro laarin kan jakejado
iwọn otutu ibiti.
Nítorí náà, olùsọdipúpọ̀ ìwọ̀ntúnwọ̀nsì ti ṣeto láti jẹ́ olùsọdipúpọ̀ ní ìwọ̀n àyè kan láàárín
23 ~ 53 °C, ṣugbọn 1 × 10-6/K, aropin iwọn otutu iye laarin 0 ~ 100 °C, tun le
wa ni gba fun awọn iwọn otutu olùsọdipúpọ.
3) Agbara elekitiroti lodi si bàbà laarin 1 ~ 100 °C tun jẹ kekere, ni isalẹ + 2 μV/K, ati
ṣe afihan iduroṣinṣin to dara julọ ni akoko ti ọpọlọpọ ọdun.
4) Ti eyi ba ni lati lo bi ohun elo resistance konge, itọju otutu otutu kekere jẹ
ti a beere lati se imukuro processing distortions o kan bi ninu ọran ti Manganin waya CMW.