Kanth-al LT alapapo waya resistance wire ferritic ironchromiumaluminium FeCrAl alloy
ileru fecral resistance alapapo waya
Fe-Cr-Al Alloy
Igbesi aye iṣẹ otutu giga to gun
Superior ifoyina resistance
Resistance ti o ga
Didara to gaju Owo kekere FeCrAl Alloy Waya
Fe-Cr-Al alloy ni ihuwasi ti resistivity giga, ilodisi iwọn otutu kekere, iwọn otutu ti n ṣiṣẹ, egboogi-ifoyina ti o dara ati ipata labẹ iwọn otutu giga.
O jẹ lilo pupọ ni ileru ile-iṣẹ, awọn ohun elo ile, ileru ile-iṣẹ, irin-irin, ẹrọ, ọkọ ofurufu, ọkọ ayọkẹlẹ, ologun ati awọn ile-iṣẹ miiran ti n ṣe awọn eroja alapapo ati awọn eroja resistance.
nichrome alapapo alloy pẹlu nickel mimọ, NiCr alloy, Fe-Cr-Al alloy ati Ejò nickel alloy.
FeCrAl resistance waya ite: 0Cr25Al5, 1Cr13Al4, 0Cr23Al5, 0Cr27Al7Mo2, 0Cr21Al6Nb, 0Cr21Al4, 0Cr21Al6.
Ni irisi okun waya, ribbon ati rinhoho, iru ohun elo Fe-Cr-Al alloy.
Okun waya: 0.018mm-10mm
Ọpa: 8mm-50mm
Ribbon: 0.05 * 0.2mm-2.0 * 6.0mm
Rinhoho: 0.5 * 5.0mm-5.0 * 250mm
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr19Al3 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Iṣiro Kemikali (%) | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | anfani | anfani | anfani | anfani | anfani | anfani | anfani | |
| Fe | Sinmi | Sinmi | Sinmi | Sinmi | Sinmi | Sinmi | Sinmi | |
| – | – | – | – | – | Nb0.5 | Mo1.8-2.2 | ||
| O pọju.lemọlemọfún iṣẹ otutu.ti eroja(%) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity ni 20℃(μΩ*m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Ìwúwo (g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Imudara igbona (KJ/m * h * ℃) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | – | |
| Imugboroosi awọn ila (α*10-6/℃) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Ibi yo isunmọ.(℃) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Agbara fifẹ (N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Ilọsiwaju ni rupture (%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Iyatọ agbegbe (%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Tun igbohunsafẹfẹ atunse (F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Lile (HB) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| akoko iṣẹ lemọlemọfún (Awọn wakati / ℃) | – | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic be | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Awọn ohun-ini oofa | Oofa | Oofa | Oofa | Oofa | Oofa | Oofa | Oofa | |