0cr21al6nb Iwọn otutu giga Fecral Alloy Electric Alapapo Resistance Waya fun Iyẹwu / Tuber Furnace adiro Ifihan Aworan
  • 0cr21al6nb Iwọn otutu giga Fecral Alloy Electric Alapapo Resistance Waya fun Iyẹwu / adiro ileru tuber

0cr21al6nb Iwọn otutu giga Fecral Alloy Electric Alapapo Resistance Waya fun Iyẹwu / adiro ileru tuber

Apejuwe kukuru:


  • Awoṣe RARA:resistohm 145
  • Ilẹ:Imọlẹ, Acid White, Oxidation
  • Ìwúwo:7.1 g/cm3
  • Atako:1.45
  • Ohun elo:Fe-Cr-Al Waya
  • Aami-iṣowo:TANKII
  • Ipilẹṣẹ:China
  • Koodu HS:72230000

    • Alaye ọja

    FAQ

    ọja Tags

    Kan-thal A-1 awọn ọja okun waya tutu-nla ni o le ṣee lo fun ileru resistance otutu otutu. Iwa ti fihan pe: ilana ọja jẹ iduroṣinṣin, iṣẹ iṣọpọ dara. Ni resistance ifoyina otutu ti o dara ati igbesi aye iṣẹ to gun; Awọn ohun-ini yiyi ti o dara julọ ni sisẹ iwọn otutu yara, irọrun ti idọti sisẹ; kekere rebound resilience ati be be lo. Ṣiṣẹ ṣiṣe ṣiṣe dara pupọ; Iwọn otutu ti nṣiṣẹ le de ọdọ 1400ºC.
    Awọn pato ati awọn lilo:

    Awọn pato ọja ti o ṣe deede: 0.5 ~ 10 mm

    Nlo: ni akọkọ ti a lo ninu ileru irin lulú, ileru itankale, igbona tube radiant ati gbogbo iru ara alapapo ileru otutu giga.

    ELEMENTI KẸKẸMIKÚN akọkọ ati awọn ohun-ini

    Awọn ohun-ini \ Ipele
    Cr Al Re Fe
    25.0 6.0 Dara Iwontunwonsi
    Iwọn otutu Iṣẹ Ilọsiwaju ti o pọju(ºC) Opin 1.0-3.0 Iwọn ila opin ti o tobi ju 3.0,
    1225-1350ºC 1400ºC
    Resisivity 20ºC (ohm*mm2/m) 1.45
    Ìwúwo (g/cm3) 7.1
    Isunmọ Oju Iyọ (ºC) 1500
    Ilọsiwaju (%) 16-33
    Tẹ Igbohunsafẹfẹ Tẹ leralera (F/R) 20ºC 7-12
    Akoko Iṣẹ Itẹsiwaju labẹ 1350ºC Diẹ sii ju wakati 60 lọ
    Micrographic Be Ferrite
    Ibasepo laarin iwọn otutu ti o pọju ati oju-aye ileru
    Ileru Afẹfẹ gbẹ Afẹfẹ ọriniinitutu hydrogen-argon Argon Jijeji
    bugbamu gaasi amonia gaasi
    Iwọn otutu(ºC) 1400 1200 1400 950 1200