Uns K93600 Invar 36 Ribbon Precision Expansion Alloy Flat Waya
Iwọn K93600 Invar36 Ribbon konge Imugboroosi Alloy Flat Waya
(Orukọ ti o wọpọ:Invar, FeNi36, Invar Standard, Vacodil36)
4J36 (Invar), ti a tun mọ ni gbogbogbo bi FeNi36 (64FeNi ni AMẸRIKA), jẹ ohun alumọni nickel-iron ti o ṣe akiyesi fun alasọdipupo kekere alailẹgbẹ rẹ ti imugboroosi gbona (CTE tabi α).
4J36 (Invar) ni a lo nibiti o nilo iduroṣinṣin onisẹpo giga, gẹgẹbi awọn ohun elo konge, awọn aago, awọn iwọn jigijigi, awọn fireemu iboju ojiji tẹlifisiọnu, awọn falifu ninu awọn mọto, ati awọn iṣọ antimagnetic. Ni wiwa ilẹ, nigbati aṣẹ-akọkọ (tito-giga) ipele igbega ni lati ṣe, oṣiṣẹ Ipele (ọpa ipele) ti a lo jẹ ti Invar, dipo igi, gilaasi, tabi awọn irin miiran. Invar struts ni a lo ni diẹ ninu awọn pistons lati ṣe idinwo imugboroja igbona wọn ninu awọn silinda wọn.
4J36 lo alurinmorin oxyacetylene, itanna arc alurinmorin, alurinmorin ati awọn ọna alurinmorin miiran. Niwọn bi olusọdipúpọ ti imugboroosi ati akopọ kemikali ti alloy jẹ ibatan yẹ ki o yago fun nitori alurinmorin fa iyipada ninu akopọ alloy, o dara julọ lati lo Argon arc alurinmorin awọn irin kikun awọn irin ni pataki ni 0.5% si 1.5% titanium, lati le din weld porosity ati kiraki.
Akopọ deede%
| Ni | 35 ~ 37.0 | Fe | Bal. | Co | - | Si | ≤0.3 |
| Mo | - | Cu | - | Cr | - | Mn | 0.2 ~ 0.6 |
| C | ≤0.05 | P | ≤0.02 | S | ≤0.02 |
olùsọdipúpọ ti imugboroosi
| θ/ºC | α1/10-6ºC-1 | θ/ºC | α1/10-6ºC-1 |
| 20 ~-60 | 1.8 | 20-250 | 3.6 |
| 20 ~-40 | 1.8 | 20-300 | 5.2 |
| 20 ~-20 | 1.6 | 20-350 | 6.5 |
| 20 ~-0 | 1.6 | 20-400 | 7.8 |
| 20-50 | 1.1 | 20-450 | 8.9 |
| 20 ~ 100 | 1.4 | 20-500 | 9.7 |
| 20-150 | 1.9 | 20-550 | 10.4 |
| 20-200 | 2.5 | 20 ~ 600 | 11.0 |
Awọn ohun-ini Aṣoju ti ara
| Ìwúwo (g/cm3) | 8.1 |
| Agbara itanna ni 20ºC(OMmm2/m) | 0.78 |
| Iwọn otutu ti resistivity (20ºC ~ 200ºC) X10-6/ºC | 3.7 ~ 3.9 |
| Imudara igbona, λ/ W/(m*ºC) | 11 |
| Ojuami Curie Tc/ºC | 230 |
| Modulu rirọ, E/Gpa | 144 |
| Ilana itọju ooru | |
| Annealing fun wahala iderun | Kikan si 530 ~ 550ºC ki o si mu 1 ~ 2 wakati. Tutu si isalẹ |
| annealing | Ni ibere lati se imukuro lile, eyi ti o wa ni mu jade ni tutu-yiyi, tutu iyaworan ilana. Annealing nilo kikan si 830 ~ 880ºC ni igbale, di 30 min. |
| Ilana imuduro |
|
| Àwọn ìṣọ́ra |
|
Aṣoju Mechanical-ini
| Agbara fifẹ | Ilọsiwaju |
| Mpa | % |
| 641 | 14 |
| 689 | 9 |
| 731 | 8 |
Iwọn otutu ifosiwewe ti resistivity
| Iwọn iwọn otutu, ºC | 20-50 | 20 ~ 100 | 20-200 | 20-300 | 20-400 |
| AR/ 103 *ºC | 1.8 | 1.7 | 1.4 | 1.2 | 1.0 |