Waya alapin Ni80Cr20 Nichrome alloy NiCr 8020 fun awọn ohun elo ile Aworan ti a fihan
  • Waya alapin Ni80Cr20 Nichrome alloy NiCr 8020 fun awọn ohun elo ile
  • Waya alapin Ni80Cr20 Nichrome alloy NiCr 8020 fun awọn ohun elo ile
  • Waya alapin Ni80Cr20 Nichrome alloy NiCr 8020 fun awọn ohun elo ile
  • Waya alapin Ni80Cr20 Nichrome alloy NiCr 8020 fun awọn ohun elo ile
  • Waya alapin Ni80Cr20 Nichrome alloy NiCr 8020 fun awọn ohun elo ile
  • Waya alapin Ni80Cr20 Nichrome alloy NiCr 8020 fun awọn ohun elo ile

Waya alapin Ni80Cr20 Nichrome alloy NiCr 8020 fun awọn ohun elo ile

Àpèjúwe Kúkúrú:


Àlàyé Ọjà

Awọn ibeere ti a maa n beere nigbagbogbo

Àwọn àmì ọjà

Ohun èlò NiCr80/20NikróòmùAlloy Waya Alapin lati Ile-iṣẹ

Àpèjúwe Ọjà
Ipele: Ni80Cr20, tí a tún ń pè ní MWS-650, NiCrA, Tophet A, HAI-NiCr 80, Chromel A, Alloy A, N8, Resistohm 80, Stablohm 650, Nichorme V àti bẹ́ẹ̀ bẹ́ẹ̀ lọ.

Akoonu Kemika(%)

C P S Mn Si Cr Ni Al Fe Òmíràn
Max
0.03 0.02 0.015 0.60 0.75~1.60 20.0~23.0 Bál. Àṣejù 0.50 Àṣejù 1.0 -

Awọn Ohun-ini Imọ-ẹrọ ti waya nichrome

Iwọn otutu Iṣẹ Ti o pọju: 1200ºC
Agbara resistance 20ºC: 1.09 ohm mm2/m
Ìwọ̀n: 8.4 g/cm3
Ìgbékalẹ̀ Ooru: 60.3 KJ/m·h·ºC
Isodipupo ti Imugboroosi Ooru: 18 α×10-6/ºC
Ojuami Yo: 1400ºC
Gbigbọn: O kere ju 20%
Ìṣètò Micrographic: Austenite
Ohun ìní oofa: ti kii ṣe magnetic

Awọn Okunfa Iwọn otutu ti Resistance Itanna

20ºC 100ºC 200ºC 300ºC 400ºC 500ºC 600ºC
1 1.006 1.012 1.018 1.025 1.026 1.018
700ºC 800ºC 900ºC 1000ºC 1100ºC 1200ºC 1300ºC
1.01 1.008 1.01 1.014 1.021 1.025 -

 Iwọn deede ti waya alloy nickel:

A n pese awọn ọja ni apẹrẹ waya, waya alapin, ati okun waya. A tun le ṣe awọn ohun elo ti a ṣe adani gẹgẹbi awọn ibeere olumulo.

Waya didan ati funfun–0.025mm~3mm

Waya pickling: 1.8mm ~ 10mm

Waya ti a ti sọ di oxidized: 0.6mm ~ 10mm

Waya alapin: sisanra 0.05mm ~ 1.0mm, iwọn 0.5mm ~ 5.0mm