FeCrAl 0cr23al5 alapapo alapin okun waya & rinhoho nipasẹ ile-iṣẹ
FeCrAl 0cr23al5 alapapo ano alapin waya & amupu;adikalanipa factory
| Ipele | 0Cr23Al5 |
| Iwọn | sisanra: 0.05-3mm iwọn: 4-250mm |
| Dada | imọlẹ slitting |
| Iwọn | 1-3kg / eerun, ni ibamu si iye awọn onibara |
| Resistivity | 1.3±0.05μΩ.m |
| Lile (HV) | 180-210HV |
| Ilọsiwaju | ≥16% |
| Ipele | Iwọn otutu ti o ga julọ | Resistivity | Lile | Agbara fifẹ | Ilọsiwaju |
| 0Cr13Al4 | 1050℃ | 1.25± 0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr15Al5 | 1100 ℃ | 1.3±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr21Al6Nb | 1300 ℃ | 1.42± 0.05μΩ.m | 200-240HV | 750N/mm2 | ≥12 |
| Cr20Ni80 | 1200 ℃ | 1.09±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr15Ni60 | 1150℃ | 1.12± 0.05μΩ.m | 175-210HV | 750N/mm2 | ≥20 |
| Cr20Ni35 | 1100 ℃ | 1.04± 0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr25Ni20(310S) | 1100 ℃ | 0.86±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Ipele | Akopọ kemikali% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0Cr15Al5 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | iwontunwonsi |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | iwontunwonsi |
| 0Cr13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | iwontunwonsi |
| Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | iwontunwonsi | 0.5 | ≤1.0 |
| Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | 0.5 | iwontunwonsi |
| Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | iwontunwonsi |
| Cr25Ni20 | 0.08 | 0.045 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | - | iwontunwonsi |
Shanghai Tankii ALloy Ohun elo Co., Ltd. idojukọ lori isejade ti nichrome alloy, thermocouple waya, fecral alloy, konge alloy, Ejò nickel alloy, gbona sokiri alloy ati be be lo ni awọn fọọmu ti waya, dì, teepu, rinhoho, opa ati awo.