Dia 0.6mm Alloy M25 Ejò Beryllium onirin fun olubasọrọ Bridges
ọja Apejuwe
Kemikali Tiwqn (Iwọn ogorun) tiC17200 Beryllium Ejò Alloy:
| Ifijiṣẹ Solutions | ||||||
| Alloy | Beryllium | Kobalti | Nickel | Co + Ni | Co+Ni+Fe | Ejò |
| C17200 | 1.80-2.00 | - | 0.20 min | 0.20 min | 0.60 ti o pọju | Iwontunwonsi |
Akiyesi: Ejò pẹlu awọn afikun dogba 99.5% Min.
TAwọn ohun-ini ti ara ti C172:
iwuwo (g/cm3): 8.36
Iwuwo ṣaaju ki o to di lile ọjọ-ori (g/cm3): 8.25
rirọ Modul (kg / mm2 (103): 13.40
Olùsọdipúpọ̀ Ìmúgbòòrò gbóná (20°C sí 200°C m/m/°C): 17 x 10-6
Gbona Conductivity (cal/ (cm-s-°C): 0.25
Yo Range (°C): 870-980
Ibinu ti o wọpọ ti a pese:
| CuBeryllium yiyan | ASTM | Mechanical ati Electrical Properties of Ejò Beryllium rinhoho | ||||||
| Orúkọ | Apejuwe | Agbara fifẹ (Mpa) | Agbara ikore 0.2% aiṣedeede | Elongation Ogorun | LARA (HV) | LARA Rockwell B tabi C Iwọn | Electrical Conductivity (% IACS) | |
| A | TB00 | Ojutu Annealed | 410-530 | 190-380 | 35-60 | <130 | 45-78HRB | 15-19 |
| 1/2 H | TD02 | Idaji Lile | 580-690 | 510-660 | 12-30 | 180-220 | 88-96HRB | 15-19 |
| H | TD04 | Lile | 680-830 | 620-800 | 2-18 | 220-240 | 96 ~ 102HRB | 15-19 |
| HM | TM04 | Mill le | 930-1040 | 750-940 | 9-20 | 270-325 | 28 ~ 35HRC | 17–28 |
| SHM | TM05 | 1030-1110 | 860-970 | 9-18 | 295-350 | 31 ~ 37HRC | 17–28 | |
| XHM | TM06 | 1060-1210 | 930-1180 | 4 ~15 | 300-360 | 32 ~ 38HRC | 17–28 | |
Imọ-ẹrọ bọtini ti Beryllium Copper(Ooru itọju)
Itọju igbona jẹ ilana pataki julọ fun eto alloy yii. Lakoko ti gbogbo awọn ohun elo bàbà jẹ lile nipasẹ iṣẹ tutu, bàbà beryllium jẹ alailẹgbẹ ni jijẹ lile nipasẹ itọju iwọn otutu kekere ti o rọrun. Ó wé mọ́ àwọn ìgbésẹ̀ pàtàkì méjì. Ni igba akọkọ ti ni a npe ni ojutu annealing ati awọn keji, ojoriro tabi ọjọ ori lile.
Solusan Annealing
Fun CuBe1.9 alloy aṣoju (1.8-2%) alloy naa jẹ kikan laarin 720°C ati 860°C. Ni aaye yii beryllium ti o wa ninu jẹ pataki "tituka" ni matrix Ejò (alafa alpha). Nipa piparẹ ni iyara si iwọn otutu yara, ọna ojutu to muna ni idaduro. Ohun elo ti o wa ni ipele yii jẹ rirọ pupọ ati ductile ati pe o le ṣiṣẹ ni imurasilẹ tutu nipasẹ iyaworan, ṣiṣe yiyi, tabi akọle tutu. Iṣiṣẹ mimu ojutu jẹ apakan ti ilana ni ọlọ ati kii ṣe deede lo nipasẹ alabara. Iwọn otutu, akoko ni iwọn otutu, oṣuwọn parẹ, iwọn ọkà, ati lile jẹ gbogbo awọn aye pataki pupọ ati pe TANKII ni iṣakoso ni wiwọ.
Ogoro Hardening
Lile ọjọ-ori ṣe pataki mu agbara ohun elo pọ si. Idahun yii ni a ṣe ni gbogbogbo ni awọn iwọn otutu laarin 260°C ati 540°C da lori alloy ati awọn abuda ti o fẹ. Yiyipo yii nfa ki beryllium ti tuka lati ṣaju bi ipele ọlọrọ beryllium (gamma) ninu matrix ati ni awọn aala ọkà. O jẹ idasile ti itusilẹ yii eyiti o fa alekun nla ni agbara ohun elo. Ipele ti awọn ohun-ini ẹrọ ti o jẹ ipinnu nipasẹ iwọn otutu ati akoko ni iwọn otutu. O yẹ ki o mọ pe Ejò beryllium ko ni awọn abuda ti ogbo otutu otutu yara.